Two-Part Fine Filling Paste

Definition:

• Two-Part Fine Filling Paste -LSP 784 002 A2-

Product Description

The two-part fine filling paste is a very fine thixotropic polyester filling paste.

This filling paste is suitable for small repairs.

Application Instructions

Properties

• Fine and non-porous
• Removes easily
• Sands easily
• High elasticity for touching up synthetic surfaces

Base Surface

Suitable base surfaces:

• Steel
• Aluminum
• Glass fiber reinforced plastics
• Old paint and factory paint
• Hardened two-part filler/two-part primers
• Plastic parts glaze-primed with Two-Part Plastic Adhesive Filler -LKF 696 009 A2-/-LKF 696 040 A2- or Adhesion Promoter -ALO 822 000 10-
• Primed surfaces with two-part polyester filling paste.

Caution

This filling paste may not be applied to PVB (acid-hardening) adhesive primers or one-part primers (for example, synthetic resin).

Application on thermoplastic or elastic coatings is also not possible. In these cases, only apply filler paste to bare steel.

Pre-treatment of base surfaces:

• Remove any grease and sand the surface.
• Bare metallic base surfaces are to be insulated with Two-Part Wash Primer -LHV 043 000 A2- and then filled with Two-Part HS Performance Filler. Sand the filler after drying.
• With UP-GF underbodies, clean components of any residual agents and sand the surface.

• Use a suitable cleaning agent before reworking to ensure a clean and residue-free surface.

Processing

Application type:

• Apply filling paste.

Mixture ratio:

• Add 2 to 3 % by weight Two-Part Hardener -LVM 018 000 A1/A2- or, especially when dealing with high temperatures, Two-Part Hardener, Long -LVM 018 100 A2-.

Note

Avoid using excessive hardener paste, to prevent it from bleeding through, especially on daylight colors and light metallic colors.

Curing Time:

• At +20 ºC (68 ºF) room temperature for about three to five minutes.

Reaction Temperature:

• Minimum +5 ºC (41 ºF)

Drying

Air Drying:

• At +20 ºC (68 ºF) room temperature for about 20 to 30 minutes.

Infrared drying:

• Short-wave heaters for three minutes (at 50 % power)
• Medium-wave heaters for five minutes.

Sanding compatibility

In connection with the aforementioned drying time:

• Dry-sand the pre-sanding with P180-240 grit sandpaper
• Dry-sand the final sanding with P240-320 grit sandpaper

• While wet, sand the pre-sanding with P240-320 sandpaper
• While wet, sand the final sanding with P600-800 sandpaper

Note

• When wet-sanding, make sure to wipe and dry off the surface.
• Temperature resistance up to +80 ºC (176 ºF).

Reworking

Recommended structure:

• One-Part Wash Primer -LVM 044 007 A2-/-LVM 044 171 A2-
• Two-Part Wash Primer -LHV 043 000 A2- and Two-Part HS Vario Filler
• Two-Part Plastic Adhesive Filler -LKF 696 009 A2-/-LKF 696 040 A2-
• Unelasticized Adhesion Promoter -ALO 822 000 10- and Two-Part HS Filler (for plastic parts)

• Then paint over with the top coat.

Personal Protective Equipment:

• Note the safety data sheets
• Wear the personal protective equipment during application

Characteristics

Delivery Viscosity	pasty
Flashpoint:	Filling paste over 23 ºC (73.4 ºF)
VOC value: 2004/42/IIB(b)(250)170	The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 250 g/L volatile organic compounds. The VOC-value of this product in ready-to-use form is a maximum of 170 g/L.

Storage

The guaranteed shelf life is 12 months from the production date. Use no later than the date indicated on the label and store in original container at +20 ºC (68 ºF).

Storage Conditions

• Storage Temperature +20 ºC (68 ºF) (temperature should not exceed +30 ºC (86 ºF) ).