Two-Part HS Brilliant Plus Clear Coat

Definition:

• Two-Part HS Brilliant Plus Clear Coat -LZK 769 K05 A5-

Product Description

Two-part HS brilliant clear coat is a high-gloss, VOC compliant high solid clear coat from the two-part acrylic system.

Properties:

• Can be used in a number of ways
• High stability
• Polishes very well
• Good spreading properties
• Good gloss and depth.
• Processing in two spray applications (preferred), (1.5 spray applications possible)

Application Instructions

Base Surface

Suitable preliminary coatings:

• Water-based base paints

Processing

Mixture ratio:

3:1 by volume with:

• Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
• Two-Part VHS Hardener, Short -LHA 009 050 A2-
• Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
• Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-
• The choice of hardener depends on the temperature and the size of the surface. See technical application information two-part VHS hardener.

Dilutable with:

• Clear Coat
• HS Spot Thinner -LVM 006 000 A2-
• See the HS spot thinner technical application information.

Processing time/pot life:

• Ready to spray in 75 to 90 minutes at +20 ºC (68 ºF)

Application type "coat"

• Processing viscosity 4 mm for +20 ºC (68 ºF), German Industry Standardization 53211

Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" is the mixed viscosity.

Adding 5 % Clear Coat Additive -LVM 007 000 A2- at +20 ºC (68 ºF) material temperature

Note

• When using as a clear coat for minimal damage repairs (clever repair procedure), 5 % Clear Coat Additive -LVM 007 000 A2- can be replaced with 5 % HS Spot Thinner -LVM 006 000 A2-.
• The mixture for the clever repair procedure described above should not be used on reclined surfaces.

• Use a measuring stick to mix when pouring in the thinner.
• Set spray nozzle (see manufacturer's information): "Compliant" 1.2 to 1.3 mm.
• Set spray nozzle (see manufacturer's information): "HVLP" 1.2 to 1.3 mm.
• Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
• Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.

• Can be applied in two spray applications with a 5 to 10 minute intermediate ventilation time. The first spray application is applied lightly, but completely.
• Apply 1.5 spray applications. The first half spray application should form a thin, nearly complete film upon which a fully-completed spray application can be applied.

• The recommended dry layer thickness is between 50 and 70 um.

Drying

Air dry at between +18 and 22 ºC (64.4º and 71.6 ºF) room temperature:

• Dry overnight

Final drying time with forced drying is a minimum of 5 to 10 minutes.

Forced drying is at between +60 and 65 ºC (140º and 149 ºF) for 30 to 35 minutes.

Final drying time for IR drying is a minimum of 5 to 10 minutes.

IR dry with short-wave heater for 10 to 15 minutes

Special Instructions

Elastification for rigid and semi-rigid plastics:

• The base material must first be mixed with 15 % Elastic Additive -ALZ 011 001-.
• Mixture with two-part VHS hardeners, 3:1 with 5 % Clear Coat Additive -LVM 007 000 A2- (drying period is lengthened).

Personal Protective Equipment:

• Note the safety data sheets
• Wear the personal protective equipment during application

Characteristics

Flashpoint:	above +23 ºC (73.4 ºF)
VOC value: 2004/42/IIB(d)(420)420	The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 420 g/L volatile organic compounds. The VOC-value of this product in ready-to-use form is a maximum of 420 g/L.

Storage

The guaranteed shelf life is:

• 48 months from date of manufacture for Two-Part HS Brilliant Plus Clear Coat -LZK 769 K05 A5-.
• 24 months from date of manufacture for Clear Coat Additive -LVM 007 000 A2-.

Use no later than the date indicated on the label and store in original container at +20 ºC (68 ºF).